eKonferencije.com: Influence of synthesis conditions on adsorption capacity of SBA-15/alginate adsorbent for removal ions of nickel(II) and lead(II) from aqueous solution

Influence of synthesis conditions on adsorption capacity of SBA-15/alginate adsorbent for removal ions of nickel(II) and lead(II) from aqueous solution

1. Đurica Katnic, University of Belgrade, Vinča Institute of Nuclear Sciences, Serbia, Serbia
2. Maja Kokunešoski, Serbia
3. Aleksandra Šaponjić, Serbia
4. Ana Valenta Šobot, Serbia
5. Milica Pošarac Marković, Serbia

Abstract: Among different ordered mesoporous silicas, SBA-type silicas are the most frequently studied. SBA-15 is an interesting mesoporous silica material having highly ordered nanosize pores and a large surface area so is widely used as absorbents, catalyst supports and drug delivery materials. Alginate as suitable biopolymer supporters improves the inappropriate physical form of mesoporous SBA-15 for practical purposes. Immobilization in polymeric matrix increases the chemical and mechanical stability of mesoporous SBA-15. Influence of synthesis conditions on adsorption capacity of SBA-15/alginate adsorbent for removal ions of nickel (II) and lead (II) from aqueous solution was investigated. Two forms of SBA-15/alginate adsorbent were prepared. Alginate gel was prepared using calcium chloride solution. Adsorption capacity behavior ions of nickel (II) and lead (II) on the two types of SBA-15/alginate adsorbent was carried out using inductively coupled plasma optical emission spectrometry (ICP-OES). Obtained results were compared with results for similar SBA-15/alginate adsorbents.

Кључне речи :

Тематска област: СИМПОЗИЈУМ Б - Биоматеријали и наномедицина

Датум: 29.06.2021.

Contemporary Materials 2021 - Савремени материјали

Датотека уз рад  (64.00 KB)


Остали радови са конференције


Претражи радове

https://www.high-endrolex.com/10