eKonferencije.com: INFLUENCE OF PROCESS PARAMETERS ON THE FRICTION COEFFICIENT IN ONE AND MULTI PHASE STEEL STRIP DRAWING IRONING TEST

INFLUENCE OF PROCESS PARAMETERS ON THE FRICTION COEFFICIENT IN ONE AND MULTI PHASE STEEL STRIP DRAWING IRONING TEST

1. Srbislav Aleksandrovic, Факултет инжењерских наука Универзитета у Крагујевцу, Serbia
2. Slaviša Djačić, Montenegro
3. Milentije Stefanović, Faculty of Engineering, University of Kragujevac, Sestre Janjić 6, 34000 Kragujevac, Srbija 2IMW Ins, Serbia
4. Milan Đorđević, Serbia
5. Vukić Lazić, Факултет инжењерских наука Универзитета у Крагујевцу, Serbia
6. Dušan Arsić, Faculty of Engineering, University of Kragujevac, Sestre Janjić 6, 34000 Kragujevac, Srbija 2IMW Ins, Serbia

Part of the experimental results of influence on friction in the stripe ironing process with double thinning are presented in this paper. Applied was Schlosser model for evaluating influence of lateral force, contact pressure, average absolute roughness height and thinning strain on friction coefficient. Applied was classical model because of sufficient intensity of drawing and lateral force. If a lateral and drawing forces are small, classical model is not suitable and give unreal negative friction coefficient values. 20 mm wide and 2.5 mm thick strips of mild steel DC04 sheets were used in the single, three and four-phase process with a maximum thinning deformation of about 29%. Appropriate lubricant, mineral oil, was used in conditions of lower speed of 20 mm/min. Three and four phase process was realized with variable lateral force of 5, 10, 15 and 20 kN.
The applied experimental test procedure enables the precise quantification of lateral force, contact pressure, thinning strain and roughness influence on friction to be established. Test also enables evaluation of lubricants quality.

Кључне речи :

Тематска област: Production and Computer-Aided Technologies

Датум: 17.02.2017.

13th International Conference on Accomplishments in Mechanical and Industrial Engineering

Датотека уз рад  (9.21 MB)


Остали радови са конференције


Претражи радове

https://www.high-endrolex.com/10